Elongation At Break
7.5 % -
Flexural Modulus
2000 MPa 290 ksi -
Flexural Strength
100 MPa 15 ksi -
Cauterization Residual Ash Content
1.5 %
Elongation At Break
7.5 %Flexural Modulus
2000 MPa 290 ksiFlexural Strength
100 MPa 15 ksiCauterization Residual Ash Content
1.5 %